HOME | 제품규격 | 마르텐사이트계
마르텐사이트계
| JIS/KS (SUS/ STS) |
ASTM/ AISI |
DIN (WNr.) |
기타 규격 |
Chemical Composition (wt%) |
Mechanical Properties (As Solution Treated) |
용도 | ||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| C | Si | Mn | P | S | Ni | Cr | Mo | Cu | N | Others | Y.S (N/㎟) |
T.S (N/㎟) |
EL. (%) |
RA. (%) |
HB | |||||
| 403 | 403 | (1.4024) | 11.5 | 샤프트,밸브 | ||||||||||||||||
| 0.15 | 0.5 | 1.0 | 0.04 | 0.03 | 0.6 | 13.0 | 200 | |||||||||||||
| 410 | 410, F6A | (1.4006) | (B7B4A, C) |
11.5 | ||||||||||||||||
| 0.15 | 1.0 | 1.0 | 0.04 | 0.03 | 0.6 | 13.5 | 200 | |||||||||||||
| JIS/KS (SUS/STS) |
ASTM/ AISI |
DIN (WNr.) |
기타 규격 |
Chemical Composition (wt%) |
Mechanical Properties (As Solution Treated) |
용도 | ||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| C | Si | Mn | P | S | Ni | Cr | Mo | Cu | N | Others | Y.S (N/㎟) |
T.S (N/㎟) |
EL. (%) |
RA. (%) |
HB | |||||
| 416 | 416 | (1.4005) | 0.15 | 12.0 | 밸브 OA기기 |
|||||||||||||||
| 0.15 | 1.0 | 1.25 | 0.06 | 0.6 | 14.0 | 0.6 | 200 | |||||||||||||
| 1.4005 | 0.06 | 0.15 | 12.0 | |||||||||||||||||
| 0.15 | 1.0 | 1.5 | 0.04 | 0.35 | 14.0 | 0.6 | ||||||||||||||
| JIS/KS (SUS/STS) |
ASTM/ AISI |
DIN (WNr.) |
기타 규격 |
Chemical Composition (wt%) |
Mechanical Properties (As Solution Treated) |
용도 | ||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| C | Si | Mn | P | S | Ni | Cr | Mo | Cu | N | Others | Y.S (N/㎟) |
T.S (N/㎟) |
EL. (%) |
RA. (%) |
HB | |||||
| 420 | (1.4021) | 0.15 | 12.0 | 각종 샤프트 |
||||||||||||||||
| 1.0 | 1.0 | 0.04 | 0.03 | 14.0 | 255 (Cold) |
|||||||||||||||
| 420J1 | 0.16 | 12.0 | ||||||||||||||||||
| 0.25 | 1.0 | 1.0 | 0.04 | 0.03 | 0.6 | 14.0 | 223 | |||||||||||||
| 420J2 | (1.4028) | 0.26 | 12.0 | |||||||||||||||||
| 0.40 | 1.0 | 1.0 | 0.04 | 0.03 | 0.6 | 14.0 | 235 | |||||||||||||
| 420F | 420F | 0.26 | 0.15 | 12.0 | 420F(ASTM) C0.3 ~0.4, Ni≤0.5 |
|||||||||||||||
| 0.40 | 1.0 | 1.25 | 0.06 | 0.6 | 14.0 | 0.6 | 235 | |||||||||||||
| JIS/KS (SUS/STS) |
ASTM/ AISI |
DIN (WNr.) |
기타 규격 |
Chemical Composition (wt%) |
Mechanical Properties (As Solution Treated) |
용도 | ||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| C | Si | Mn | P | S | Ni | Cr | Mo | Cu | N | Others | Y.S (N/㎟) |
T.S (N/㎟) |
EL. (%) |
RA. (%) |
HB | |||||
| 431 | 431 | 1.25 | 15.0 | 선박샤프트 항공기부품 |
||||||||||||||||
| 0.2 | 1.0 | 1.0 | 0.04 | 0.03 | 2.50 | 17.0 | 302 | |||||||||||||
| JIS/KS (SUS/STS) |
ASTM/ AISI |
DIN (WNr.) |
기타 규격 |
Chemical Composition (wt%) |
Mechanical Properties (As Solution Treated) |
용도 | ||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| C | Si | Mn | P | S | Ni | Cr | Mo | Cu | N | Others | Y.S (N/㎟) |
T.S (N/㎟) |
EL. (%) |
RA. (%) |
HB | |||||
| 440A | 0.60 | 16.0 | ||||||||||||||||||
| 0.75 | 1.0 | 1.0 | 0.04 | 0.03 | 0.6 | 18.0 | 0.75 | 255 | ||||||||||||
| 440B | 0.75 | 16.0 | ||||||||||||||||||
| 0.95 | 1.0 | 1.0 | 0.04 | 0.03 | 0.6 | 18.0 | 0.75 | 255 | ||||||||||||
| 440C | 440C | 0.95 | 16.0 | 베어링 펌프부품 |
||||||||||||||||
| 1.20 | 1.0 | 1.0 | 0.04 | 0.03 | 0.6 | 18.0 | 0.75 | 269 | ||||||||||||
| F6NM | 0.5 | 3.5 | 11.5 | 0.5 | 620 | 790 | 15 | 45 | ||||||||||||
| 0.05 | 0.6 | 1.0 | 0.03 | 0.03 | 5.5 | 14.0 | 1.0 | 295 | ||||||||||||
| F9 | 0.5 | 0.3 | 8.0 | 0.9 | 380 | 585 | 20 | 40 | 179 | |||||||||||
| 0.15 | 1.0 | 0.6 | 0.03 | 0.03 | 10.0 | 1.10 | 217 | |||||||||||||
| F91 | 1.4903 | 0.08 | 0.2 | 0.3 | 8.0 | 0.85 | 0.03 | Nb0.06 ~0.1 |
415 | 585 | 20 | 40 | 단조밸브 | |||||||
| 0.12 | 0.5 | 0.6 | 0.02 | 0.01 | 0.4 | 9.5 | 1.05 | 0.07 | 248 | |||||||||||
| F92 | 0.07 | 0.3 | 8.5 | 0.3 | 0.03 | Nb0.04 ~0.09, V0.15 ~0.25 |
440 | 620 | 20 | 45 | ||||||||||
| 0.13 | 0.5 | 0.6 | 0.02 | 0.01 | 0.4 | 9.5 | 0.6 | 0.07 | W1.5 ~2.0, B0.001 ~0.006 |
269 | ||||||||||